Sub-ablative Er,Cr:YSGG laser irradiation under all-ceramic restorations: effects on demineralization and shear bond strength

Abstract

This study evaluated the caries resistant effects of sub-ablative Er,Cr:YSGG laser irradiation alone and combined with fluoride in comparison with fluoride application alone on enamel prepared for veneer restorations. And also, evaluated these treatments' effects on the shear bond strength of all-ceramic veneer restorations. One hundred and thirty-five human maxillary central teeth were assigned to groups of 1a-control, 1b-laser treated, 1c-fluoride treated, 1d-laser + fluoride treated for shear bond testing and to groups of 2a-positive control(non-demineralised), 2b-laser treated, 2c-fluoride treated, 2d-laser + fluoride treated, 2e-negative control (demineralised) for microhardness testing (n = 15, N = 135). Demineralisation solutions of microhardness measurements were used for the ICP-OES elemental analysis. The parameters for laser irradiation were as follows: power output, 0.25 W; total energy density, 62.5 J/cm(2) and energy density per pulse, 4.48 J/cm(2) with an irradiation time of 20 s and with no water cooling. Five percent NaF varnish was used as fluoride preparate. ANOVA and Tukey HSD tests were performed (alpha = 5%). Surface treatments showed no significant effects on shear bond strength values (p = 0.579). However, significant differences were found in microhardness measurements and in elemental analysis of Ca and P amounts (p < 0.01). Surface-treated groups showed significantly high VNH values and significantly low ICP-OES values when compared with non-treated (-control) group while there were no significance among surface-treated groups regarding VHN and ICP-OES values. Sub-ablative Er,Cr:YSGG treatment alone or combined with fluoride is as an effective method as at least fluoride alone for preventing the prepared enamel to demineralization with no negative effect on shear bond strength.