Yazar "Sivrikaya, Burak" seçeneğine göre listele

Listeleniyor 1 - 3 / 3
  • Küçük Resim
    Öğe
    Comparison of short- and long-term ASR test methods on cementitious composites
    (2020) Sivrikaya, Burak; Demir, İlhami; Sevim, Özer
    Concrete has a significant place in construction structures, is a material that can be easily damaged due to incorrect design, incorrect material selection. Concrete may be damaged by physical and chemical factors. One of these factors is the alkali-silica reaction (ASR). ASTM C1260, is a short-term test method, and ASTM C227, is a longterm test method, are used to measure effect of alkali-silica reaction. In this study, the effect of fly ash additive use with 0, 5, 10, 15, and 20 wt.% replacement of cement was investigated in short- and long-term ASR test methods. For this purpose, while samples prepared for ASTM C1260 were kept in NaOH solution 14-days, samples prepared for ASTM C227 were waited 360-days in normal water solution. As a result; mortar bars with 20% fly ash additive ratio were classified as harmless for ASR in both test methods.
  • Küçük Resim
    Öğe
    A study on ASR mitigation by optimized particle size distribution
    (ELSEVIER SCI LTD, 2020) Demir, Ilhami; Sivrikaya, Burak; Sevim, Ozer; Baran, Mehmet
    In this study, the effect of alkali-silica reaction on binary cementitious composite systems incorporating fly ash or slag having optimized particle size distribution has been investigated. Specimens have been exposed to ASR effect according to ASTM C227 and ASTM C1260 methods. Test results, which were conducted after ASR exposure, have been discussed in terms of use of additive having optimized particle size distribution. The characterization of specimens was investigated using scanning electron microscopy (SEM) coupled with energy dispersive X-ray spectroscopic analyzer (EDS), Fourier-transform infrared spectroscopy (FTIR) and thermogravimetric analysis instrument (TGA). As a result of the experimental program, it was seen that the ASR effect is reduced with fly ash and slag replacement. Even, fly ash addition has been more effective than slag addition in reducing the ASR effect for the same additive ratio. In addition, addition of fly ash and slag with optimized particle-size distribution were found to be more effective in reducing the ASR effect as compared to addition of fly ash and slag without optimized particle-size distribution. (C) 2020 Elsevier Ltd. All rights reserved.
  • Küçük Resim
    Öğe
    Tane dağılımı optimize edilmiş puzolanların alkali silika reaksiyonuna etkisi
    (Kırıkkale Üniversitesi, 2018) Sivrikaya, Burak; Demir, İlhami
    İnşaat sektöründe oldukça önemli bir yere sahip olan beton, çevresel ve kimyasal etmenlerden dolayı zamanla deforme olmaktadır. Bu kimyasal etmenlerden biriside Alkali Silika Reaksiyonu (ASR)' dur. Alkali silika reaksiyonu, çimentoda bulunan alkali oksitler ve agrega içerisindeki reaktif silisin yeterli nem miktarında kimyasal tepkimeye girerek alkali silika jeli oluşturmasıyla başlar. Yüksek su emme özelliğine sahip bu jeller, zaman içerisinde çok fazla su absorbe ederek hacimsel olarak büyür ve betonun içsel gerilmesini artırarak betonda kılcal çatlaklar oluşmasına yol açar. Bu çatlaklar betonu ve içerisindeki donatıyı çevresel faktörlere (iklim değişikliği, donma çözülme vs. gibi) mâruz bırakarak servis ömrünün kısalmasına yol açmaktadır. Bu çalışmada, tane dağılımı optimize edilmiş yüksek fırın cürufu (YFC) ve F sınıfı uçucu külün (UK) alkali silika reaksiyonuna (ASR) etkisi incelenmiştir. Çimento malzemesi yerine, Çatalağzı Termik Santralinden alınan uçucu kül ve Zonguldak Ereğli Demir Çelik Fabrikası atığı olan yüksek fırın cürufu kullanılmıştır. Agrega olarak ise, aktif silis içeriği çeşitli çalışmalarla belirlenen İzmir Gediz bölgesine ait dere agregası kullanılmıştır. Bu çalışmada; çimento yerine % 5, % 10, % 15, % 20 oranlarında yüksek fırın cürufu ve uçucu kül ikame edilerek, farklı numunelere aynı oranlarda tane dağılımı optimize edilmiş yüksek fırın cürufu ve uçucu kül ikame edilerek alkali silika reaksiyonu etkisi araştırılmıştır. Yapılan deneysel çalışma sonucunda, tane dağılımı optimize edilmiş uçucu kül ve yüksek fırın cürufunun tane dağılımı optimize edilmemiş yüksek fırın cürufu ve uçucu küle göre alkali silika reaksiyonunu azaltmada daha etkili olduğu görülmüştür.