    Tailored pore structures and mechanical properties of porous alumina ceramics prepared with corn cob pore-forming agent
    (WILEY, 2021) Dele-Afolabi, T. T.; Hanim, M. A. Azmah; Ojo-Kupoluyi, O. J.; Calin, R.; Zuhri, M. Y. M.
    In this work, the effects of porosity and different particle sizes of pore-forming agent on the mechanical properties of porous alumina ceramics have been reported. Different grades of porous alumina ceramics were developed using corn cob (CC) of different weight contents (5, 10, 15, and 20 wt%) and particle sizes (<63 mu m, 63-125 mu m and 125-250 mu m) as the pore-forming agent. Experimental results showed that total porosity and pore cavity size of the porous alumina ceramics increased with rising addition of CC pore former. Total porosity increased with increasing particle size of CC with the Al2O3-(<63)CC(5)sample exhibiting the lowest total porosity of 41.3 vol% while the highest total porosity of 68.1 vol% was exhibited by the Al2O3-125-250CC20. The particle size effect of CC on the mechanical properties revealed that diametral tensile strength and hardness of the porous alumina ceramics deteriorated with increasing particle size of CC pore former. The Al2O3-(<63)CC(5)sample exhibited the highest diametral tensile strength and hardness of 25.1 MPa and 768.2 HV, respectively, while Al2O3-(125-250)CC(20)exhibited the lowest values of 1.1 MPa and 35.9 HV. Overall, porous alumina ceramics with the smallest pore sizes under each particle size category exhibited superior mechanical properties in their respective categories.