    Cytotoxicity and apoptotic effects of nickel oxide nanoparticles in cultured HeLa cells
    (Via Medica, 2010) Ada, Kezban; Turk, Mustafa; Oguztuzun, Serpil; Kilic, Murat; Demirel, Mehmet; Tandogan, Nisa; Latif, Ozturk
    The aim of this study was to observe the cytotoxicity and apoptotic effects of nickel oxide nanoparticles on human cervix epithelioid carcinoma cell line (HeLa). Nickel oxide precursors were synthesized by an nickel sulphate-excess urea reaction in boiling aqueous solution. The synthesized NiO nanoparticles (<200 nm) were investigated by X-ray diffraction analysis and transmission electron microscopy techniques. For cytotoxicity experiments, HeLa cells were incubated in 50-500 mu g/mL NiO for 2, 6, 12 and 16 hours. The viable cells were counted with a haemacytometer using light microscopy. The cytotoxicity was observed low in 50-200 mu g/mL concentration for 16 h, but high in 400-500 mu g/mL concentration for 2-6 h. HeLa cells' cytoplasm membrane was lysed and detached from the well surface in 400 mu g/mL concentration NiO nanoparticles. Double staining and M30 immunostaining were performed to quantify the number of apoptotic cells in culture on the basis of apoptotic cell nuclei scores. The apoptotic effect was observed 20% for 16 h incubation.
  • Küçük Resim
    Öğe
    Nikel oksit (NiO) tozlarının hazırlanması ve adsorplama özelliklerinin belirlenmesi
    (Kırıkkale Üniversitesi, 2009) Demirel, Mehmet; Bostan, Kezban Ada
    Derişimi 0.05?0.30 molL?1 arasında değişen farklı NiSO4.6H2O çözeltileri aşırı ölçüde üre ile kaynatılarak homojen çöktürme ile NiO tozları hazırlanmıştır. Hazırlanan örnekleri elektron mikroskopisi (SEM), diferansiyel termal ve termogravimetrik analiz ( TG-DTA), X-ışınları difraksiyonu (XRD) ve partikül boyut dağılımı analizi teknikleri ile incelenerek bulunan sonuçlar tartışılmıştır. Azotun 77 K'deki adsorpsiyon ve desorpsiyonundan sırayla belirlenen özgül yüzey alanı ve özgül gözenek hacmi gibi adsorplama özelliklerinin derişim ile değişimi tartışılmıştır.