Mekanokimyasal yöntem ile enerjik madde olarak kullanılabilen magnezyum diborür (mgb2) sentezi

Basit Öğe Kaydı
dc.contributor.advisorGürü, Metin
dc.contributor.authorCanöz, Bilal
dc.date.accessioned2021-01-16T19:04:21Z
dc.date.available2021-01-16T19:04:21Z
dc.date.issued2017
dc.departmentKKÜ, Fen Bilimleri Enstitüsü, Savunma Teknolojileri Anabilim Dalı
dc.description.abstractBu çalışmanın amacı, mekanokimyasal yöntem ile Magnezyum diborür (MgB2) sentezinin araştırılmasıdır. Magnezyum diborür, roket yakıtlarında başlatıcı ve hızlandırıcı olarak kullanılmaktadır. Bu nedenle, yüksek verimlilikte veya saflıkta sentezlenmesi savunma sanayinde önemli bir yer tutmaktadır. Bu çalışmada, Magnezyum diborür sentezi, elementel magnezyum (Mg) ve elementel Bor (B) kullanılarak gerçekleştirildi. Mekanokimyasal yöntem ile yapılan deneyler, bilyeli öğütücü kullanılarak Argon gazı atmosferinde gerçekleştirildi. İşlem sonunda elde edilen ürün, X-Işını Kırınım yöntemi (XRD), Taramalı Elektron Mikroskopisi (SEM-EDS) kullanılarak analiz edildi. Öğütücüden elde edilen numunelerin X-ışını kırınımı desenlerinde MgB2'e ait pik gözlendi. Öğütücüden alınan numune, 700°C sıcaklığında Argon atmosferinde sinterlendi. Sinterleme işlemi sonunda safsızlık oluşturan diğer fazların uzaklaştırılması için farklı derişimlerde HCl çözeltileri ile 30 dakika liç işlemi uygulandı ve 0,1 M HCl çözeltisinin saflaştırma için yeterli olduğu belirlendi. Ayrıca, bilya-toz oranı, öğütme süresi gibi parametrelerin etkisi incelenerek, reaksiyon girdilerinin stokiyometrik oranda bulunduğu, 8:1 bilye/toz oranı ve 7 saat öğütme süresi optimum koşullar olarak belirlendi.en_US
dc.description.abstractThe purpose of this study is to investigate magnesium diboride synthesis by mechanochemical method. Magnesium diboride is used as an initiator and accelerator in rocket fuels, and has an important place in high-yielding or purity-based defense industry. Magnesium diboride synthesis was carried out using elementary magnesium (Mg), elementary boron (B). The experiments carried out by mechanochemical method were carried out using Argon gas using a ball mill. The product obtained at the end of the process was analyzed by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM-EDS). MgB2 peaks were observed in the product diagrams as a result of X-ray diffraction analysis. The product was then sintered in an Argon atmosphere at a temperature of 700 oC. In order to remove impurities leaching was carried out with HCl solutions at different concentrations for 30 min at the end of the sintering process and 0,1 M HCl solution was found to be sufficient for purification. The effect of milling parameters such as the ball-to-powder ratio and the grinding time was also investigated, and the 8:1 ball-to-powder ratio and 7-hour grinding time were determined as optimum conditions. The effect of milling parameters such as the ball-to-powder ratio and the grinding time was also investigated, and the 8:1 ball-to-powder ratio and 7-hour grinding time were determined as optimum conditions.en_US
dc.identifier.endpage67en_US
dc.identifier.startpage1en_US
dc.identifier.uri
dc.identifier.urihttps://hdl.handle.net/20.500.12587/16086
dc.identifier.yoktezid476579
dc.language.isotr
dc.publisherKırıkkale Üniversitesien_US
dc.relation.publicationcategoryTezen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectSavunma ve Savunma Teknolojilerien_US
dc.subjectDefense and Defense Technologiesen_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.subjecten_US
dc.titleMekanokimyasal yöntem ile enerjik madde olarak kullanılabilen magnezyum diborür (mgb2) sentezien_US
dc.title.alternativeSynthesis of magnesium diboride (mgb2) that will be used as an energetic material by mechanochemical methoden_US
dc.typeMaster Thesisen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim
İsim:
476579.pdf
Boyut:
1.66 MB
Biçim:
Adobe Portable Document Format
Açıklama:
Tam metin/fulltext
İndir

Koleksiyon

Fen Bilimleri Enstitüsü Tez Koleksiyonu