Evaluation of the push-out bond strength of ProRoot MTA and Biodentine after removal of calcium hydroxide and triple antibiotic paste
[ X ]
Tarih
2018
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Aim: To evaluate the effect of calcium hydroxide (CH) and triple antibiotic paste (TAP) on the push-out bond strength of ProRoot® MTA and Biodentine®. Methodology: Root canals of 120 human teeth were instrumented using rotary files. To obtain a standard diameter of 1.5 mm, the roots were instrumented with a #6 Peeso reamer. The reamers passed 1 mm beyond the apex point to simulate open apices. The roots were randomly assigned into the following groups: Group 1 was administered calcium hydroxide (CH); Group 2 was administered triple antibiotic paste (TAP); and Group 3 was a control group and had no medicament. The medicaments were removed after 3 weeks. Thereafter, the specimens were divided into two subgroups (n = 20) according to which calcium silicate-based cement, ProRoot MTA (Dentsply Maillefer, Ballaigues, Switzerland) or Biodentine (Septodont, France), was applied. The push-out test was performed, and the data were analyzed statistically using one-way ANOVA and by Tukey’s post hoc test. Results: In both the ProRoot MTA and Biodentine groups, pairwise comparisons between medicaments showed similar values to the control group (p>0.05). Overall, there was a predominance of cohesive failures between root dentin and the cements. Conclusions: ProRoot MTA and Biodentine showed similar bond strength values, and prior application of TAP or CH did not affect the bond strength significantly.
Açıklama
Anahtar Kelimeler
Kaynak
International Dental Research
WoS Q Değeri
Scopus Q Değeri
Cilt
8
Sayı
2