Fe-22.3% Ni-2.7 % mn alaşımında martensite oluşumunun mösbaver spektrometresi ile incelenmesi

Basit Öğe Kaydı
dc.contributor.advisorZengin, D. Mehmet
dc.contributor.authorGüngüneş, Hakan
dc.date.accessioned2021-01-16T19:16:49Z
dc.date.available2021-01-16T19:16:49Z
dc.date.issued2001
dc.departmentKKÜ, Fen Bilimleri Enstitüsü, Konu:Fizik ve Fizik Mühendisliği = Physics and Physics Engineering Dizin:Düşük sıcaklık = Low temprature ; Faz geçişleri = Phase transitions ; Martensit = Martensite ; Mössbauer spektrumu = Mössbauer spectrum
dc.description.abstractÖZET Yüksek Lisans Tezi Fe-22.3%Nİ-2.7%Mn ALAŞIMINDA MARTENSİTE OLUŞUMUNUN MÖSSBAUER SPEKTROMETRESİ İLE İNCELENMESİ Hakan GÜNGÜNEŞ Kırıkkale Üniversitesi Fen Bilimleri Enstitüsü Fizik Anabilim Dalı Danışman: Prof. Dr. D. Mehmet ZENGİN 2001,Sayfa:59 Jüri: Prof. Dr. D. Mehmet ZENGİN Prof. Dr. İhsan ULUER Prof. Dr. Hüseyin AKTAŞ Fe-22.3%Ni-2.7%Mn alaşımında soğutma etkisi ile ortaya çıkan martensitik faz geçişleri Mössbauer Spektrometresi kullanılarak incelenmiştir. Bu amaçla 25 (im kalınlığında hazırlanıp austenite fazda kristalleştirilen örneğin oda sıcaklığında Mössbauer Spektrumu alınmıştır. Daha sonra sıvı azot içerisinde bir hafta bekletilen örneğin oda sıcaklığında yeniden Mössbauer Spektrumu alındı. Sonuçta austenite fazdaki örneğin oda sıcaklığında hala austenite fazda bulunduğunu, ama sıvı azot'ta bir hafta bekletilmesi sonucu örnekte austenite miktarının 75.982%' lik kısmının martensite dönüştüğü gözlendi dolayısıyla martensite fazın oluştuğu sonucuna varıldı. Anahtar Kelimeler: Austenite-Martensite faz geçişi, Mössbauer Spektrumu, Düşük Sıcaklıken_US
dc.description.abstractABSTRACT Masters Thesis THE INVESTIGATION OF THE MARTENSITE TRANSFORMATIONS IN Fe-22.3%Ni-2.7Mn ALLOYS USING BY MÖSSBAUER SPECTROMETER Hakan GÜNGÜNEŞ Kırıkkale Üniversitesi Graduate School of Natural and Applied Sciences Department of Physics Supervisor: Prof. Dr. D. Mehmet ZENGİN 2001,Page:59 Jüri: Prof. Dr. D. Mehmet ZENGİN Prof. Dr. İhsan ULUER Prof. Dr. Hüseyin AKTAŞ Martensite phase tansformations obtained from cooling effect in Fe-22.3%Ni- 2.7%Mn alloy have been investigated using by Mössbauer Spectrometer. In this study, a Mössbauer spectrum of a sample with 25 um thickness crystallized in austenite phase has been taken at room temperature. After that measurement the same sample has been waited for a week at liquid nitrogen temperature and then the Mössbauer spectrum of the sample has been taken again. As a result, the sample in austenite phase was still in austenite phase at room temperature. But the part of 75.982% of the sample that was kept for a week at liquid nitrogen temperature has been transformed to the martensite phase. So it has concluded that martensite phase has been obtained. Key Words: Austenite-martensite phase transformation, Mössbauer spectrum, Low temperatureen_US
dc.identifier.citationBu tezin, veri tabanı üzerinden yayınlanma izni bulunmamaktadır. Yayınlanma izni olmayan tezlerin basılı kopyalarına Üniversite kütüphaneniz aracılığıyla (TÜBESS üzerinden) erişebilirsiniz.en_US
dc.identifier.endpage59en_US
dc.identifier.startpage1en_US
dc.identifier.urihttps://hdl.handle.net/20.500.12587/17646
dc.identifier.yoktezid105850
dc.language.isotr
dc.publisherKırıkkale Üniversitesien_US
dc.relation.publicationcategoryTezen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectFizik ve Fizik Mühendisliğien_US
dc.subjectPhysics and Physics Engineeringen_US
dc.titleFe-22.3% Ni-2.7 % mn alaşımında martensite oluşumunun mösbaver spektrometresi ile incelenmesien_US
dc.typeMaster Thesisen_US

Dosyalar

Koleksiyon

Fen Bilimleri Enstitüsü Tez Koleksiyonu