Investigation of Sintering Behaviour of Bone China Bodies Produced by Bone China Wastes
[ X ]
Tarih
2019
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Kırıkkale Üniversitesi
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Flawedand broken wastes obtained from the production of Bone China were used forformulating bone china body recipe instead of albite, quartz and bone ash asthe same chemical composition of original bone china body. The amount of kaolinand clay were used as the same amount of the bone china body due to obtainoptimum plastic behaviour. This study was carried out in two steps. At thefirst step, compositions were fired at the original firing temperature of bonechina as 1250 °C and at the second step, compositions were fired at 1200 °C. Theraw and fired strength, water absorption and pyroplastic deformation results ofthe bodies were measured. The phase and microstructural evoluation of thebodies were determined by XRD and SEM.As the amount of the bone china wasteincreased amount of the glassy phase increased, anorthite and quartz were decreased. Technical properties of thebodies changed parallel to the microstructural changes. As the amount of bonewaste increased in the compositions, optimum technical properties of thecompositions were obtained at 1200 °C .
Açıklama
Anahtar Kelimeler
Bone china, Bone ash, Bone china waste, Microstructure
Kaynak
Uluslararası Mühendislik Araştırma ve Geliştirme Dergisi
WoS Q Değeri
Scopus Q Değeri
Cilt
1
Sayı
2-481