An Investigation of Wear Behaviours of Mg Matrix Composites Reinforced Carbon Nanotube Produced by Powder Metallurgy Method

Basit Öğe Kaydı
dc.contributor.authorYıldırım, Musa
dc.contributor.authorÖzyürek, Dursun
dc.date.accessioned2025-01-21T14:20:52Z
dc.date.available2025-01-21T14:20:52Z
dc.date.issued2021
dc.description.abstractIn this study, production, and wear behaviours of AZ91-carbon nanotube reinforced metal matrix composites by powder metallurgy method were investigated. Composite powders were produced by multi wall carbon nanotube powders (four different amount) were added to AZ91 Mg. Produced composite powders were pre-formed by cold press then they were sintered at 550 ºC for 1 hour. Sintered samples were characterized. Wear tests were done by pin-on disc type wear device under 30 N load with three sliding distances. At the end of the study, it was seen that hardness values were increased with increasing carbon nanotube amount. The maximum hardness value was measured in the 0.25% carbon nanotube added sample. However, according to wear test, the weight loss values were increased with increasing reinforcement amount due to non-homogenous distribution and occurred agglomeration of reinforcement. The maximum weight loss values were measured in added 2 % sample.
dc.description.abstractToz metalurjisi yöntemi ile AZ91-Karbon nanotüp takviyeli metal matrisli kompozitlerin üretimi ve aşınma davranışlarının incelendiği bu çalışmada, AZ91 Magnezyum alaşımına çok duvarlı karbon nanotüp ilave edilerek kompozit tozlar üretilmiştir. Üretilen kompozit tozlar soğuk preslenerek ön şekillendirilmiş arkasından 550 ºC’de 1 saat sinterlenmiştir. Sinterlenen kompozitlerin karakterizasyon çalışmaları yapılmıştır. Pin-on disk tipi aşınma cihazında 30 N yük altında üç farklı kayma mesafesinde aşınma testleri yapılmıştır. Yapılan çalışmalar sonucunda karbon nanotüp ilave edilen kompozitlerde sertlik değerinin arttığı en yüksek sertlik %0,25 karbon nanotüp ilave edilen kompozitte elde edilmiştir. Ancak yapılan aşınma testleri sonucunda takviye elemanının yapı içerisinde homojen dağılmaması ve oluşan aglomerasyonlar sonucu ilave edilen takviye miktarıyla aşınmanın arttığı, ağırlık kaybındaki en yüksek değer %2 karbon nanotüp takviyeli kompozitte elde edilmiştir.
dc.identifier.dergipark1038336
dc.identifier.doi10.29137/umagd.1038336
dc.identifier.issn1308-5514
dc.identifier.issue3-1
dc.identifier.startpage8
dc.identifier.urihttps://dergipark.org.tr/tr/download/article-file/2139045
dc.identifier.urihttps://dergipark.org.tr/tr/pub/umagd/issue/67876/1038336
dc.identifier.urihttps://doi.org/10.29137/umagd.1038336
dc.identifier.urihttps://hdl.handle.net/20.500.12587/19291
dc.identifier.volume1
dc.language.isotr
dc.publisherKırıkkale Üniversitesi
dc.relation.ispartofUluslararası Mühendislik Araştırma ve Geliştirme Dergisi
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_20241229
dc.subjectMg matrix composites
dc.subjectcarbon nanotube
dc.subjectpowder metallurgy
dc.subjectwear behaviours
dc.subjectMg matrisli kompozit
dc.subjectkarbon nanotüp
dc.subjecttoz metalürjisi
dc.subjectaşınma davranışları
dc.subjectMaterials Engineering (Other)
dc.titleAn Investigation of Wear Behaviours of Mg Matrix Composites Reinforced Carbon Nanotube Produced by Powder Metallurgy Method
dc.title.alternativeToz Metalurjisi Yöntemiyle Üretilen Karbon Nanotüp Takviyeli Mg Matrisli Kompozitlerin Aşınma Davranışlarının İncelenmesi
dc.typeArticle

Dosyalar

Koleksiyon

Uluslararası Mühendislik Araştırma ve Geliştirme Dergisi
TR-Dizin İndeksli Yayınlar Koleksiyonu