Mechanical and Formaldehyde-related Properties of Medium Density Fiberboard with Zeolite Additive

Basit Öğe Kaydı
dc.contributor.authorCamlibel, Osman
dc.date.accessioned2021-01-14T18:10:21Z
dc.date.available2021-01-14T18:10:21Z
dc.date.issued2020
dc.departmentKKÜ
dc.description.abstractZeolite was investigated as a potential component in the production of medium-density fiberboard (MDF). A mixture of beech (40%), oak (30%), and pine (30%) wood chips was used for fiber production. Chips were cooked for 4 min in an Asplund defibrator with a vapor pressure of 8 bar, and a temperature of 180 degrees C. Chemicals were added on fibers in the blow line. The resins were added at 11 wt% based on oven-dried wood fibers. Ammonium sulphate was added at 0.72 wt% based on resins. Paraffin wax was added as 1.8 wt% based on resin. Zeolite was prepared in a separate tank for its use instead of lignocellulosic fibers in the production of 1 m(3) MDF. The fibers were dried to 12% moisture. A temperature of approximately 190 degrees C and a pressure of approximately 32 kg.m(-2) were applied to the mixture for 280 s to make MDF panels (500 x 490 x 14 mm). Mechanical properties of MDF boards were significantly increased for bending (MOE) and elastic modulus (MOR), but a little negatively affected on internal bond (16), physical properties were negatively increased thickness swelling (ThS) and water absorption (WA). Consequently, increasing zeolite minerals in MDF boards showed best results of formaldehyde emission properties of MDF.en_US
dc.identifier.citationCamlibel, O. (2020). "Mechanical and formaldehyde-related properties of medium density fiberboard with zeolite additive," BioRes. 15(4), 7918-7932.en_US
dc.identifier.doi10.15376/biores.15.4.7918-7932
dc.identifier.endpage7932en_US
dc.identifier.issn1930-2126
dc.identifier.issue4en_US
dc.identifier.scopus2-s2.0-85129204144
dc.identifier.scopusqualityQ3
dc.identifier.startpage7918en_US
dc.identifier.urihttps://doi.org/10.15376/biores.15.4.7918-7932
dc.identifier.urihttps://hdl.handle.net/20.500.12587/12534
dc.identifier.volume15en_US
dc.identifier.wosWOS:000583802900045
dc.identifier.wosqualityQ2
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.language.isoen
dc.publisherNORTH CAROLINA STATE UNIV DEPT WOOD & PAPER SCIen_US
dc.relation.ispartofBIORESOURCES
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectMDFen_US
dc.subjectZeoliteen_US
dc.subjectFormaldehyde emissionen_US
dc.subjectPhysical propertiesen_US
dc.subjectMechanical propertiesen_US
dc.titleMechanical and Formaldehyde-related Properties of Medium Density Fiberboard with Zeolite Additiveen_US
dc.typeArticle

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim
İsim:
Mechanical and formaldehyde-related properties of medium density fiberboard with zeolite additive.pdf
Boyut:
386.36 KB
Biçim:
Adobe Portable Document Format
Açıklama:
Tam Metin/Full Text
İndir

Koleksiyon

WOS İndeksli Yayınlar Koleksiyonu
Makale Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu